Database of Zeolite Structures
 
Framework Type TSC
Powder Diffraction Pattern for Tschörtnerite
Input Parameters
  Wavelength:  or
  2θ range:
  Step size:
  Polarization factor:
  Background:
  Reference peak is
    peak closest to °2θ
    reflection (hkl)
       scaled to
  Intensity axis:
     
Peak shape
  Pseudo-Voigt: (1-n)Gaussian + n Lorentzian
  FWHM = sqrt (U + V tan θ + W tan2θ)
  Mixing parameter (n): %
  Peak range: FWHM
  Peak width:
       set UVW at: U =   V =   W =
       Calculate UVW such that FWHM =
    FWHM =
       FWHM =
   
Select Output
 
List hkl and intensity
List powder pattern
plot powder pattern
Crystal Data
  Space Group: F m -3 m   (# 225)   
  Cell parameters: a = 31.62 Å b = 31.62Å c = 31.62 Å
    α = 90° β = 90° γ = 90 °
  Chemical Formula |Ca64(K2,Ca,Sr,Ba)48Cu48 (OH)128 (H2O)x| [Al192Si192O768]-TSC
  Refinement: Single Crystal X-ray Refinement. Rp = 0.065, Rwp = 0.156
  Reference: Effenberger, H., Giester, G., Krause, W. and Bernhardt, H.J.
Am. Mineral., 83, 607-617 (1998)
  Atomic Coordinates:          
   
Atom
Form Factor
x
y
z
PP
B(iso)
   
  Si1
Si
0.10993 0.18083 0.24967 0.5 0.92
  Al1
Al
0.10993 0.18083 0.24967 0.5 0.92
  Si2
Si
0.05044 0.12239 0.19243 0.5 0.95
  Al2
Al
0.05044 0.12239 0.19243 0.5 0.95
  O1
O
0.0674 0.15559 0.23003 1 1.51
  O2
O
0.21169 0.21169 0.13239 1 1.37
  O3
O
0.21022 0.21022 0.40798 1 1.32
  O4
O
0.1464 0.1464 0.26611 1 1.72
  O5
O
0.14402 0.14402 0.05687 1 2.08
  O6
O
0.0772 0.0772 0.19159 1 2.01
  O7
O
0.11259 0.20286 0 1 2.05
  Ca1
Ca
0.09965 0.09965 0.09965 1 2.04
  Ca2
Ca
0.20984 0.20984 0.20984 1 1.23
  K1
K
0.17945 0.27909 0 0.125 2.68
  Ca3
Ca
0.17945 0.27909 0 0.125 2.68
  Sr1
Sr
0.17945 0.27909 0 0.125 2.68
  Ba1
Ba
0.17945 0.27909 0 0.125 2.68
  Cu2
Cu
0.07339 0.07339 0 1 2.31
  OH1
O
0.04506 0.04506 0.10539 1 2.16
  OH2
O
0.28335 0.28335 0.28335 1 1.29
  Cl1
Cl
0 0 0 0.224 0.87
  O8
O
0.041 0 0 0.181 5.37
  O9
O
0.0262 0.0262 0.0262 0.243 3.95
  O10
O
0.1467 0.1467 0.1467 1 9.71
  O11
O
0.0159 0.1842 0 0.305 8.76
  O12
O
0.2087 0.2339 0 0.5 3.71
  O13
O
0.0085 0.1316 0.3048 0.22 10.42
  O14
O
0.13599 0.13559 0.13559 1 5.68
  O15
O
0.0336 0.0336 0.2642 0.195 7.9
  O16
O
0.0714 0.0888 0.3105 0.189 7.9
  O17
O
0.0514 0.1204 0.3298 0.4 16.82