Database of Zeolite Structures
 
Framework Type EWF
Powder Diffraction Pattern for EMM-25, as-made
Input Parameters
  Wavelength:  or
  2θ range:
  Step size:
  Polarization factor:
  Background:
  Reference peak is
    peak closest to °2θ
    reflection (hkl)
       scaled to
  Intensity axis:
     
Peak shape
  Pseudo-Voigt: (1-n)Gaussian + n Lorentzian
  FWHM = sqrt (U + V tan θ + W tan2θ)
  Mixing parameter (n): %
  Peak range: FWHM
  Peak width:
    set UVW at: U =   V =   W =
    FWHM =
    FWHM =
  FWHM =
   
Select Output
 
List hkl and intensity
List powder pattern
plot powder pattern
Crystal Data
  Space Group: C m c m   (# 63)   
  Cell parameters: a = 11.055 Å b = 22.912Å c = 24.914 Å
    α = 90° β = 90° γ = 90 °
  Chemical Formula |[MDPB+2]2| [B3.5Si112.5O232]-EWF
MDPB+2 = C26H58N24 = 1,4-bis(N-methyl-N,N-dipentylammonium)butane
= methyl-[4-[methyl(dipentyl)azaniumyl]butyl]-dipentylazanium
SMILES: CCCCC[N+](C)(CCCCC)CCCC[N+](C)(CCCCC)CCCCC   Images:  stick or 3D
  Refinement: cRED refinement
  Comment: disorder model
  Reference: Cho, J., Yun, Y., Xu, H., Sun, J., Burton, A.W., Strohmaier, K.G., Terefenko, G., Vroman, H., Afeworki, M., Cao, G., Wang, H., Zou, X., Willhammar, T.
Chem. Mater., 33, 4146-4135 (2021)
  Atomic Coordinates:          
   
Atom
Form Factor
x
y
z
PP
B(iso)
    
  Si1
Si
0.5 0.4667 0.066 0.5 2.29
  Si2
Si
0 0.0514 0.1622 0.5 1.58
  Si3
Si
0.5 0.477 0.2628 0.5 1.89
  Si4
Si
0 0.0521 0.3633 0.5 1.66
  Si5
Si
0.5 0.4705 0.4563 0.5 1.5
  Si6
Si
0.2388 0.1247 0.3463 0.5 1.11
  Si7
Si
0.358 0.057 0.4387 0.5 1.18
  Si8
Si
0.2356 0.4385 0.4401 0.5 1.18
  Si9
Si
0.1368 0.3681 0.1556 0.5 1.18
  Si10
Si
0.1387 0.2409 0.1892 0.5 0.87
  Si11
Si
0.2428 0.1178 0.1505 0.5 0.95
  Si12
Si
0.3566 0.064 0.055 0.5 0.95
  Si13
Si
0.2396 0.4332 0.0554 0.5 1.66
  Si14
Si
0.1436 0.3633 0.349 0.5 1.26
  Si15
Si
0.1423 0.2344 0.3139 0.5 2.13
  Si16
Si
0.2412 0.4358 0.25 1 1.78
  Si17
Si
0.3596 0.0624 0.25 1 1.18
  O1
O
0 0.0179 0.0206 0.5 2.84
  O2
O
0.5 0.496 0.1244 0.5 3.08
  O3
O
0 0.0314 0.2225 0.5 3
  O4
O
0.5 0.4992 0.3245 0.5 3.08
  O5
O
0 0.0287 0.4231 0.5 2.76
  O6
O
0.1754 0.3014 0.165 0.5 0.95
  O7
O
0.2172 0.1901 0.1542 0.5 1.5
  O8
O
0.3263 0.1093 0.1027 0.5 1.74
  O9
O
0.3822 0.4263 0.0661 0.5 2.37
  O10
O
0.204 0.4996 0.078 0.5 2.21
  O11
O
0.1722 0.4239 0.497 0.5 1.97
  O12
O
0.1684 0.3885 0.0944 0.5 1.82
  O13
O
0.1186 0.087 0.1566 0.5 1.97
  O14
O
0.3358 0.0985 0.1955 0.5 1.5
  O15
O
0.177 0.4031 0.2956 0.5 4.58
  O16
O
0.1671 0.2949 0.3479 0.5 2.13
  O17
O
0.2252 0.1884 0.3333 0.5 1.82
  O18
O
0.298 0.111 0.4063 0.5 2.05
  O19
O
0.3818 0.4342 0.4488 0.5 1.18
  O20
O
0.308 -0.0011 0.4261 0.5 2.45
  O21
O
0.2953 0.0806 0.4967 0.5 2.76
  O22
O
0.2085 0.3881 0.3986 0.5 2.45
  O23
O
0.113 0.0949 0.3603 0.5 3
  O24
O
0.2929 0.0927 0.2957 0.5 4.18
  O25
O
0.2181 0.4025 0.1953 0.5 2.29
  O26
O
0.194 0.4993 0.239 0.5 3.16
  O27
O
0.172 0.2412 0.25 1 2.29
  O28
O
0.3846 0.4364 0.2599 0.5 2.13
  O29
O
0 0.2197 0.178 0.5 1.18
  O30
O
0 0.3757 0.1679 0.5 1.97
  O31
O
0 0.2304 0.3157 0.5 2.68
  O32
O
0 0.3752 0.3576 0.5 2.76
  O33
O
0.5 0.0545 0.0624 0.5 1.58
  O34
O
0.5 0.0578 0.4517 0.5 5.29
  O35
O
0.5 0.0565 0.2599 0.5 2.76
  N1
N
0.46 0.218 0.488 0.25 47.4
  C1
C
0.68 0.213 0.511 0.25 23.7
  C2
C
0.231 0.222 0.486 0.25 103
  C3
C
0.5869 0.308 0.313 0.25 111
  C4
C
0.339 0.249 0.491 0.25 13.4
  C5
C
0.607 0.298 0.25 0.5 158
  C6
C
0.576 0.249 0.343 0.25 103
  C7
C
0.892 0.201 0.476 0.25 18.9
  C8
C
0.568 0.252 0.512 0.25 94.7
  C9
C
0.555 0.261 0.401 0.25 34.7
  C10
C
0.899 0.199 0.539 0.25 34.7
  C11
C
0.76 0.221 0.461 0.25 30
  C12
C
0.451 0.16 0.52 0.25 158
  C13
C
0.5 0.206 0.429 0.5 158


Copyright © 2017 Structure Commission of the International Zeolite Association (IZA-SC)